Anionic aqueous dispersion of rubbermaker's sulfur. Used as vulcanizer in latex compounds for adhesive applications. Use level: 1.0-3.0 parts per hundred on dry weight ... view more

Aqueous dispersion of zinc oxide. Used as accelerator in latex emulsion compounds for adhesive applications. Use level: 1.0-4.0 parts per hundred... view more

Blend of sulfur, zinc oxide, accelerator and antioxidant in aqueous dispersion. Used as accelerator for vulcanization of latex compounds for adhesive applications. Particle size, average... view more

Aqueous dispersion of rubbermaker's sulfur. Used as vulcanizer in latex compounds for adhesive applications. Use level: 2.0-3.0 parts per hundred on dry weight... view more

Aqueous dispersion of zinc oxide. Used as vulcanizer in latex emulsion compounding for adhesive applications. Use level: 1.0-4.0 parts per hundred... view more

Composite of essential ingredients necessary for the accelerated vulcanization of latex compounds. Used in adhesive applications... view more

Aqueous anionic dispersion of zinc dibenzyldithiocarbamate. Used as accelerator in latex compounding for adhesive applications. Suits for vulcanization processes where the formation of volatile... view more

Zinc di-n-butyldithiocarbamate. Used as primary accelerator and nondiscoloring antioxidant in natural and synthetic polymers for adhesives. Provides fast cure and high modulus. Use level: 1 - 1.5... view more

Aqueous dispersion of zinc dibutyldithiocarbamate. Used as accelerator and antioxidant in latex compounding for adhesives. Provides fast cure and high modulus. Use level: 1 - 1.5 parts per hundred... view more

Zinc diethyldithiocarbamate. Used as primary accelerator in natural and synthetic polymers for adhesives. Used in conjunction with equal amounts of zinc mercaptobenzothiazole. Use level: 1-1.5... view more

Aqueous anionic dispersion of zinc diethyldithiocarbamate. Used as accelerator in latex compounding for adhesive applications. Used in conjunction with equal amounts of zinc mercaptobenzothiazole... view more

Aqueous anionic dispersion of zinc dimethyldithiocarbamate. Used as accelerator in latex compounding for adhesive applications. Provides moderately fast curing with good aging properties. Use... view more

Zinc mercaptobenzothiazole. Used as primary accelerator in natural and synthetic polymers for adhesives. Commonly used as a secondary accelerator in conjunction with a dithiocarbamate. Use level:... view more

Aqueous anionic dispersion of zinc mercaptobenzothiazole. Used as accelerator in latex compounding for adhesive applications. Commonly used as a secondary accelerator in conjunction with a... view more

Synergistic blend of polymeric hindered phenol and thioester. Used as non-staining and non-discoloring antioxidant in adhesives. Provides high stabilization and antioxidant protection. Use level:... view more

Anionic emulsion of a non-staining bisphenol antioxidant. Used for SBR and Natural rubber latices. Use level: 0.25 to 2.0 parts per hundred polymer... view more

Aqueous anionic dispersion of a non-staining bisphenol antioxidant. Used in adhesives, latex films and foams. Can cause some slight pink discoloration in certain applications Use level: 0.5 to 2.0... view more

Non-staining secondary synergist thioester antioxidant, especially when used in combination with primary amine and phenolic antioxidants. Used in adhesives. Provides good stabilization and... view more

Anionic aqueous dispersion of N,N'-Di-beta-naphthyl-p-phenylenediamine. Used as semi-staining antioxidant in adhesives. Provides good heat and oxidation resistance. Protects against degradation by... view more

Aqueous anionic dispersion of 4,4'-Butylidenebis (6-tert-butyl-m-cresol). Used as antioxidant in adhesives. Provides high activity stabilization and antioxidant protection to white and light colored... view more

Aqueous dispersion of polyphenolic. Used as self-synergized, non staining antioxidant for adhesives and latex systems. Provides good stabilization and antioxidant protection... view more

Synergistic blend of polymeric hindered phenol and thioester. Used as non-staining, non-discoloring antioxidant for adhesives and latex systems. Provides very good stabilization, antioxidant... view more

Non-phenolic antioxidant mixture in emulsion. Used as slightly staining and virtually non-discoloring antioxidant in adhesives and latex systems. Possesses stability over a wide pH range for direct... view more

Aqueous dispersion of butylated reaction product of para-cresol and dicyclopentadiene. Used as non-staining and non-discoloring antioxidant. Provides highly efficient stabilization and antioxidant... view more

Aqueous dispersion of polymeric styrenated phenol. Used as non-staining and non-discoloring antioxidant. Provides good activity and persistence. Use level: 1.0 to 2.0 parts per hundred rubber... view more

Synergistic blend of polymeric hindered phenol and thioester. Used as non-staining and non-discoloring antioxidant in adhesives. Provides good stabilization and protection to synthetic and natural... view more

Butylated reaction product of para cresol and dicyclopentadiene. Used as non-staining and non-discoloring antioxidant. Provides highly efficient stabilization and antioxidant protection in many... view more

Di-n-butyl ester of maleic acid. Used as a plasticizer for vinyl resins in adhesive applications... view more

Di-isobutyl maleate. Used as plasticizer for adhesives... view more

2-ethylhexyl ester of maleic acid. Used as plasticizer in adhesives. Provides elasticity and flexibility... view more